Mineralogical and chemical characterization of DD3 kaolin from the east Algeria

Résumé

The mineralogical and chemical characteristics, based on X-ray diffraction (XRD) and scanning electron microscopy, of a kaolin known as DD3, from eastern Algeria were examined in the present study. The results showed that kaolin DD3 has an alumina content of 39%. The SiO2/Al2O3 molar ratio of 2.14 is close to that of a pure halloysite. The hematite concentration is relatively large and the flux oxides ratios remain as acceptable impurities. Microscopic observations showed a predominant tubular halloysite phase, flattened hexagonal platelets corresponding to the presence of kaolinite and its polymorphs (nacrite, dickite), and hydrated alumina. The SiO2/Al2O3 molar ratio and tubular DD3 suggest possible uses in technical ceramics and nanotechnology applications. Analysis by XRD revealed the presence of many phases. Thermal treatment at 450 °C and chemical treatment with HCl confirmed the presence of halloysite. The inclusion in the clay of organic molecules (dimethylsulfoxide (DMSO), DMF, and diluted glycerol) showed that the DMSO led to expansion of the inter-planar distance. The intercalation by DMSO molecules resulted in a shift of the basal peak from 10 to 11.02 Å and partial displacement of the peak from 3.35 to 3.65 Å. These two peaks are characteristic of halloysite. The presence of residual nacrite was also confirmed by the shift of the peak observed at 3.35 Å. A full analysis of the XRD patterns using the Match software, based on these results, showed that the DD3 clay consists of >60% halloysite.
Fichier principal
Vignette du fichier
1-s2.0-S0366317515001260-main.pdf (1.36 Mo) Télécharger le fichier
Origine : Publication financée par une institution
Licence : CC BY NC ND - Paternité - Pas d'utilisation commerciale - Pas de modification

Dates et versions

hal-03116798 , version 1 (06-07-2022)

Licence

Paternité - Pas d'utilisation commerciale - Pas de modification

Identifiants

Citer

Hamza Senoussi, Hocine Osmani, Christian Courtois, Mohamed El Hadi Bourahli. Mineralogical and chemical characterization of DD3 kaolin from the east Algeria. Boletín de la Sociedad Española de Cerámica y Vidrio, 2016, 55 (3), pp.121-126. ⟨10.1016/j.bsecv.2015.12.001⟩. ⟨hal-03116798⟩
29 Consultations
15 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More