DIELECTRIC AND PIEZOELECTRIC PROPERTIES OF LEAD-FREE ( Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 TiO 3 + x% Ce 2 O 3 + y% La 2 O 3 + z% Y 2 O 3 COMPOUNDS SYNTHESIZED BY SOL–GEL TECHNIQUE - Université Polytechnique des Hauts-de-France Accéder directement au contenu
Article Dans Une Revue Journal of Advanced Dielectrics Année : 2013

DIELECTRIC AND PIEZOELECTRIC PROPERTIES OF LEAD-FREE ( Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 TiO 3 + x% Ce 2 O 3 + y% La 2 O 3 + z% Y 2 O 3 COMPOUNDS SYNTHESIZED BY SOL–GEL TECHNIQUE

Résumé

( Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 TiO 3 + x% Ce 2 O 3 + y% La 2 O 3 + z% Y 2 O 3 compounds (named BNT–BT– x/y/z) were synthesized by a sol–gel technique, for (x,y,z) = (0,0,0), (0.25, 0.25, 0.25), (0.25, 0.5, 0.5), (0.5, 0.25, 0.25) and (0.5, 0.5, 0.25). The structural variation according to the different system compositions is investigated by X-ray diffraction analyses. The results shows that the addition of Ce 2 O 3 , La 2 O 3 or Y 2 O 3 in BNT–BT system, do not modify the crystalline structure, and a rhombohedral–tetragonal morphotropic phase boundary is maintained for different dopant addition. The BNT–BT–x/y/z-based ceramics sintered at relatively low temperature (1100°C) exhibit a good densification ratio. The optimum dielectric and piezoelectric properties are obtained with the BNT–BT–0.5/0.25/0.25 composition. High dielectric properties at room temperature (ε r > 1000) and low dielectric losses (tan δ < 4 × 10 -2 ) are obtained for this composition. This compound exhibits a piezoelectric constant d 33 of 95 pC/N, a good polarization behavior is observed with high remanent polarization P r of 9.21 μC/cm 2 and low value coercitive field E c of 2.66 kV/mm.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-04281123 , version 1 (12-11-2023)

Identifiants

Citer

A. Chaouchi, M. Saidi, S. d'Astorg, Mohamed Rguiti, Christian Courtois. DIELECTRIC AND PIEZOELECTRIC PROPERTIES OF LEAD-FREE ( Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 TiO 3 + x% Ce 2 O 3 + y% La 2 O 3 + z% Y 2 O 3 COMPOUNDS SYNTHESIZED BY SOL–GEL TECHNIQUE. Journal of Advanced Dielectrics, 2013, 02 (04), pp.1250022. ⟨10.1142/S2010135X12500221⟩. ⟨hal-04281123⟩
7 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More