Development of a mixed mode double cantilever beam specimen for the fracture characterization of adhesives under high displacement rate

Abstract

In this paper, a new specimen called mixed mode double cantilever beam (MMDCB) was developed for the mixed mode fracture characterization of adhesives under high displacement rates. The MMDCB specimen was designed using finite elements simulations in order to determine the fracture toughness for a mode mixity in the plane I+II+III. Firstly, results from MMDCB specimens tested under quasi-static loading were experimentally compared to a reference single leg bending test. The test results, obtained with the two different specimens, exhibit consistent evaluations of the mixed mode fracture toughness. Secondly, the MMDCB specimen testing under asymmetric high displacement rate was validated through explicit simulations. The corrected beam theory with effective crack length was extended to the analysis of MMDCB specimens tested under high displacement rate. It was numerically proved to accurately determine the mixed mode fracture toughness under a displacement rate up to 1 m/s.
Fichier principal
Vignette du fichier
Dagorn2020.pdf (1.97 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03446864 , version 1 (23-05-2022)

Licence

Attribution - NonCommercial

Identifiers

Cite

Noëlig Dagorn, Gérald Portemont, Julien Berthe, François Rasselet, Benjamin Bourel, et al.. Development of a mixed mode double cantilever beam specimen for the fracture characterization of adhesives under high displacement rate. Engineering Fracture Mechanics, 2021, 242, pp.107467. ⟨10.1016/j.engfracmech.2020.107467⟩. ⟨hal-03446864⟩
65 View
52 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More