Synthesis and characterization of BNT thin films prepared by sol-gel method

Résumé

Polycrystalline piezoelectric lead-free Bi0.5Na0.5TiO3 (abbreviated as BNT) thin films were deposited on Pt/TiO2/SiO2/Si substrates by an optimized Sol-Gel process. The phase structure and morphology of the as-prepared product were examined by X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscopy (SEM). The film treated at 700 °C with the rapid thermal processor (RTP) for 30 sec is dense and well crystallized in the rhombohedral perovskite phase. The dielectric constant and loss tangent at 10 kHz are 420 and 0.07%, respectively, while the remnant polarization and coercive field are 12 μC/cm2 and 120 kV/cm, respectively, at 1000 Hz.

Dates et versions

hal-03586629 , version 1 (24-02-2022)

Identifiants

Citer

Sara Abou Dargham, Freddy Ponchel, Youssef Zaatar, Jamal Assaad, Denis Remiens, et al.. Synthesis and characterization of BNT thin films prepared by sol-gel method. 12th International Conference on Nanosciences & Nanotechnologies & 8th International Symposium on Flexible Organic Electronics, NN15 & ISFOE15, Jul 2015, Thessaloniki, Greece. pp.810-815, ⟨10.1016/j.matpr.2016.02.013⟩. ⟨hal-03586629⟩
21 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More